Fire resistance rating and testing of stainless steels
The inherent oxidation resistance and elevated temperature strength of stainless steels finds useful application in buildings and structures where fire resistance is important. The most useful family of stainless steels for these applications is the austenitics, but the short-term nature of fire means that embrittlement should not be practical issue and so the ferritic and duplex families can also be considered.
As materials, stainless steels, do not have an intrinsic ‘fire rating’. Tests to assess fire resistance are done on specific fabrications under precise conditions. This is covered by BS476 parts 20, 21, (load-bearing elements), and 22, (non-load-bearing elements).
Unfortunately the design software which automatically calculates the behaviour of loaded stainless steel sections in a fire is no longer available from the Steel Construction Institute, SCI. However, any parties interested in developing a new version of that software are invited to contact Nancy Baddoo at the SCI to discuss options for taking this forward. firstname.lastname@example.org.
However, in the latest version of the the design manual for stainless steel, which can be accessed here, there is a full chapter, (no. 8), devoted to design for fire resistance This will be quite helpful for those structural design engineers who wish to understand and apply the design principles for structural stainless steels in this situation.
BS 476 covers fire testing on building materials and structures. Many of the parts of this standard are not directly relevant to stainless steels. Parts 4, 6,7, 11, 12, 13, 15 in particular are not appropriate to stainless steels as these deal with tests such as: –
combustibility, (ignitability from flame impingement or thermal irradiance)
Stainless steels are not ignitable and will also not assist in the propagation of fires by flame spread. The surface of stainless steel is normally inert and stable in oxidising conditions, such as those found in most flames and heat sources
However to satisfy the requirements of BS 476 and similar fire testing standards, tests need to be done on specific fabricated components. Stainless steel, as a material, does not carry a ‘fire rating’.
Results of fire testing on stainless steel components
Tests done for Stewart Fraser Ltd. on their fire resistant 316 type doors and frames to BS 467 part 22 showed that after 60 minutes, the temperature on the ‘safe’ side of the door only reached 98°C. (These doors have a 316 frame and contain an insulating non-combustible board filling.)
The test was terminated after 2 hours 10 minutes with the doors and frames fully intact.
The only damage was due to thermal distortion and some discoloration of the steel on the ‘safe’ side. The fire on the ‘attack’ side was fully contained by the doors for over two hours.
Tests done on 1.4362, (2304), type duplex, supplied for testing by Avesta AB 1991, and fabricated into a clad ships bulkhead, also demonstrates the fire resistance of stainless steels.
The fabricated bulkhead with a 1.5 mm thick 1.4362 corrugated profile skin and ceramic wool insulating filler performed satisfactorily under a simulated hydrocarbon fuel fire.
The ‘attack’ temperature reached 1100°C and radiated a bright orange colour after only 15 minutes. Some distortion and attendant insulation smoke were recorded during the tests, but after 40 minutes the temperature on the ‘safe’ face was still below 30°C. This surface temperature had risen to around 110°C after 60 minutes.
After 120 minutes it was noted that the test unit was continuing to satisfy the criterion, (International Maritime Organisation Resolution A517 (XIII)), for resistance to smoke and hot gases penetration.
Manufacturers of products and components for fire resisting applications should be consulted at an early stage to avoid costly design changes at a later stage.
Heat resisting properties of stainless steels
Most stainless steel grades that would be considered for building applications, i.e. the 304, (1.4301), and 316, (1.4401), types have useful, long-term oxidation resistance at temperatures over 800°C and do not begin to melt until temperatures of over 1375°C are reached. It is unlikely that uniform, sustained high temperatures like these would be reached in short term ‘transient’ fire conditions.
The short term mechanical, (tensile), strength, elastic, (Young’s), modulus and physical properties of thermal expansion and conductivity are of interest in assessing stainless steels for fire resistance.
The 304 and 316 austenitic types lose strength to about 55% of their ambient temperature levels at 700°C, the 0.2% proof strengths being around 225 to 308 MPa., (N/mm2) ,at ambient, but fall to 95 to 131 MPa., (N/mm2), at 700°C. The modulus, typically around 200 KN/mm2 at ambient temperatures, falls to around 144 KN/mm2 at 700 °C for type 304. This is significantly different from carbon steels, where the modulus at 800 °C can be as low as only 9% of the ambient value.
The higher thermal expansion rates for the austenitic stainless steels means that physical distortion can be a problem in transient fire conditions where thermal gradients are likely to be large.
The thermal conductivity of the austenitic family is lower than ferritics and although this may be useful in containing heat flow through a structure, it may contribute to thermal distortion.
Allowances for distortion and seizing of items like fire doors should be considered.