Ambient temperature mechanical properties of martensitic and precipitation hardening stainless steel long products to BS EN 10088-3

Introduction

BS EN 10088-3 gives the mechanical properties for stainless steel semi-finished products, bars, rods and sections for general purposes. This article covers martensitic and precipitation hardening stainless steels. The properties given are proof strength, tensile strength, elongation and hardness.

The data given is not intended to replace that shown in individual standards to which reference should always be made.

BS EN 10088-3:20014 Edition

BS EN 10088-3 was originally published in 1995. The second version, BS EN 10088-3:2005, has been superseded by BS EN 10088-3:2014.

The tables shown here only have the 2014 tensile property ranges of the martensitic and precipitation hardening steels. Two new grades have been added, 1.4150 and 1.4612.

The mechanical properties of the following grades were changed:
1.4313, 1.4028, 1.4122, 1.4057, 1.4606.

This article does not include bright products.

BS EN 10088-3 mechanical properties – martensitic and precipitation hardening stainless steels

 

Designation Mechanical properties min unless stated
Steel name Steel number Thickness d mm Heat treatment condition1) Proof strength Rp0.2 3) N/mm2 Tensile strength R m 3) N/mm3 Elongation A3) % Max hardness2) HB
Martensitic stainless steels-standard grades
X12Cr13 1.4006 A max. 730 220
<160 QT650 450 650/850 15
X12CrS13 1.4005 A max. 730 220
<160 QT650 450 650/850 12
X15Cr13 1.4024 A max. 730 220
<160 QT650 450 650/850 15
X20Cr13 1.4021 A max. 760 230
<160 QT700 500 700/850 13
<160 QT800 600 800/950 12
X30Cr13 1.4028 A max. 800 245
<160 QT850 650 850/1000 10
X39Cr13 1.4031 A max. 800 245
<160 QT800 650 800/1000 10
X46Cr13 1.4034 A max. 800 245
<160 QT800 650 850/1000 10
X38CrMo14 1.4419 A max. 760 235
X50CrMoV15 1.4116 A max. 900 280
X55CrMo14 1.4110 <100 A max. 950 280
X14CrMoS17 1.4104 A max. 730 220
<60 QT650 500 650/850 12
60<d<160</d QT650 500 650/850 10
X39CrMo17-1 1.4122 A max. 900 280
<60 QT750 550 750/950 12
60<d<160</d QT750 550 750/950 12
X17CrNi16-2 1.4057 A max. 950 295
<60 QT800 600 800/950 14
60<d<160</d QT800 600 800/950 12
<60 QT900 700 900/1050 12
60<d<160</d QT900 700 900/1050 10
X3CrNiMo13-4 1.4313 A 1100 320
<160 QT700 520 700/850 15
160<d<250</d QT700 520 700/850 12
<160 QT780 620 780/980 15
160<d<250</d QT780 620 780/980 12
<160 QT900 800 900/1100 12
160<d<250</d QT900 800 900/1100 10
X4CrNiMo16-5-1 1.4418 A 1100 320
<160 QT760 550 760/960 16
160<d<250</d QT760 550 760/960 14
<160 QT900 700 900/1100 16
160<d<250</d QT900 700 900/1100 14
Martensitic stainless steels-special grades
X29CrS13 1.4029 <160 A max. 800 245
<160 QT850 650 850/1000 9
X46CrS13 1.4035 < 63 A max. 800 245
X70CrMo15 1.4109 <100 A max. 900 280
X40CrMoVN 1.4123 <100 A 280
X105CrMo17 1.4125 <100 A 285
X90CrMoV18 1.4112 <100 A 265
X2CrNiMoV13-5-2 1.4415 <160 QT750 650 750/ 900 18
<160 QT850 750 850/1000 15
X53CrSiMoVN16-2 1.4150 <100 A 255
QT
Precipitation hardening stainless steels-standard grades
X5CrNiCuNb16-4 1.4542 <100 AT max. 1200 360
P800 520 800/950 18
P930 720 930/1100 16
P960 790 960/1160 12
P1070 1000 1070/1270 10
X7CrNiAl17-7 1.4568 <30 AT max. 850 255
X5CrNiMoCuNb14-5 1.4594 <100 AT max. 1200 360
P930 720 930/1100 15
P1000 860 1000/1200 10
P1070 1000 1070/1270 10
Precipitation hardening stainless steels-standard grades
X1CrNiMoAlTi12-9-2 1.4530 <150 AT max.1200 363
P1200 1100 min. 1200 12
 X1CrNiMoAlTi12-10-2 1.4596 < 150 AT max 1200 363
P1400 1300 min 1400 9
X1CrNiMoAlTi12-11-2 1.4612 < 150 AT 331
P1510 1380 min 1510 10
P1650 1515 min 1650 10
X5NiCrTiMoVB25-15-2 1.4606 < 50 AT 250 max 700 35 212
P880 550 880/1150 20

Note

  1. A= annealed; QT=quenched and tempered.
  2. Only for guidance.
  3. for rods, only the tensile strength values apply.
  4. Note 4 deleted

 